Irreplaceable "rhenium" heating device in MOCVD

Irreplaceable "rhenium" heating device in MOCVD

(Summary description)Metal Organic Chemical Vapor Deposition (MOCVD) is a chip epitaxial technology for preparing mixed semiconductor devices, metal and metal oxide and metal nitride film materials. In the MOCVD system, the crystal growth is mostly under normal pressure or low pressure (10-100 Torr), and the substrate temperature is 500 to 1200 ℃. In order to grow pure, steep interface, and good uniform thin film materials, the MOCVD equipment needs to be chemical The reaction provides a suitable environment. The heating system is an important part of the MOCVD equipment. Whether it can heat the substrate quickly and uniformly directly affects the quality of film deposition, thickness consistency, and chip performance.

Irreplaceable "rhenium" heating device in MOCVD

(Summary description)Metal Organic Chemical Vapor Deposition (MOCVD) is a chip epitaxial technology for preparing mixed semiconductor devices, metal and metal oxide and metal nitride film materials. In the MOCVD system, the crystal growth is mostly under normal pressure or low pressure (10-100 Torr), and the substrate temperature is 500 to 1200 ℃. In order to grow pure, steep interface, and good uniform thin film materials, the MOCVD equipment needs to be chemical The reaction provides a suitable environment. The heating system is an important part of the MOCVD equipment. Whether it can heat the substrate quickly and uniformly directly affects the quality of film deposition, thickness consistency, and chip performance.

Information

Metal Organic Chemical Vapor Deposition (MOCVD) is a chip epitaxial technology for preparing mixed semiconductor devices, metal and metal oxide and metal nitride film materials. In the MOCVD system, the crystal growth is mostly under normal pressure or low pressure (10-100 Torr), and the substrate temperature is 500 to 1200 ℃. In order to grow pure, steep interface, and good uniform thin film materials, the MOCVD equipment needs to be chemical The reaction provides a suitable environment. The heating system is an important part of the MOCVD equipment. Whether it can heat the substrate quickly and uniformly directly affects the quality of film deposition, thickness consistency, and chip performance.

01

The working conditions of the MOCVD heater are very harsh: long continuous working time, high temperature, high heat flux and repeated temperature rise and fall. The resistor piece is the core part of the heater. After passing a certain current, the resistor piece generates heat and becomes the heat source of the entire device. When the surface temperature of the graphite plate used to place the substrate is 1350K, the temperature of the resistance chip is as high as 2000K, and the temperature of the resistance heater can reach 2500°C or more during the heating process, so the selected material must have a high melting point, good high temperature strength, and chemical High stability characteristics. Take the MOCVD equipment for growing GaN as an example, the optimal growth temperature is about 1000~1200℃. The temperature of the heating element of the heater is about 1500~2000℃. In the process of growing GaN, the epitaxial substrate is required to rapidly increase temperature and increase temperature at a rate of 3-10°C/s) and decrease the temperature.

01

According to the process requirements of the MOCVD equipment, the performance of the heating ring must meet: 1. Realize the uniform heating of the large-size graphite tray, and the effective area ratio should cover the entire surface as much as possible; 2. The temperature rise and fall rate is fast, and the stability time is short; 3. The temperature rise and fall dynamics Keep the temperature uniform during the process; 4. For different gas flow environments, uniform heating can be achieved; 5. In the repeated temperature rise and fall use process, the structure is stable and reliable, and the service life is long.

According to the working characteristics of MOCVD, the selection of metal resistance heating elements is the most reasonable. According to the actual temperature conditions that need to be met, only a few refractory metals such as tungsten and rhenium can meet the requirements of use.

Performance name Pure tungsten Pure rhenium
Melting point/℃ 3410 3170
Density/g/cm3 19.3 21.02
Resistivity μΩ·cm 20℃ 5.5 19.8
1000℃ 36.2 62
1500℃ 52 82
2000℃ 66 150
Microhardness/MPa Processing state 3423-3923 4903-7845
1000℃ annealing 834 2256-2452
Tensile strength/MPa Processing state 1950 1600
1400℃ annealing 1650 1400
1600℃ annealing 1200 1400
1800℃ annealing 850 1400
Elongation/% Processing state 1-2 1-2
1400℃ annealing 1-2 20-25
1600℃ annealing 1-2 18-20
1800℃ annealing 1-2 10-15
Recrystallization temperature 1100℃ 1500℃

The tungsten heating device will become brittle after being recrystallized after high temperature use, and it is very easy to break under the condition of shock or vibration. Compared with tungsten, rhenium has a higher recrystallization temperature, and the recrystallized rhenium is not a brittle material, but its strength is reduced. As a non-stressed heating device, it still has good working ability and has the best high temperature stability. High creep strength. Therefore, rhenium is used to manufacture MOCVD heating devices. It is the most appropriate choice in consideration of performance and cost. No other material can replace it.

Scan the QR code to read on your phone

Online customer service
Customer service hotline
0731-88590085 0731-88590085
Service time:
8:00 - 24:00
Customer service group:
在线客服

Contact Us

 

Address: Room 401, Building 10, Xinggong Science and Technology Park, No. 100 Luyun Road, Changsha High-tech Development Zone, Hunan

Official QR Code

scan it  Follow us